TMCP AR400 Wear resistance Steel Sheet Manufacturer Hot Rolled 6mm Thick NM360 NM400 NM450 NM500 NM550 Wear Resistant Steel Plates
AR400 wear-resistant steel plate origin Wugang delivery status quenching and tempering (Q+T) (quenching and tempering)GB NM400 Wear Resistant Steel Plate Cuttable Quenched Tempered Heat Treatment Hot Rolled High Hardness 400HB Metal plate | |
Standard grade
|
DIN: XAR300,XAR400, XAR450, XAR500, XAR600, DILLIDUR400V,DILLIDUR450V,DILLIDUR500V; X120Mn12; 1.3401;
SSAB:400,450,500,550,600;WELDX700,WELDX900,WELDX960; NF: FORA400,FORA500,Creusabro4800,Creusabro8000; EN: QUARD400,QUARD450,QUARD500 ; RAEX320,RAEX400,RAEX450,RAEX500; DUrostat400,DUrostat450,DUrostat500; JIS: JFE-EH360,JFE-EH400,JFE-EH500, WEL-HARD400, WEL-HARD500; SUMIHARD-K340,SUMIHARD-K400,SUMIHARD-K500 GB: NM360,NM400,M450,NM500,NM550,NM600,NR360,NR400,B-HARD360,B-HARD400,B-HARD450,KN-55,KN-60,KN-63. |
Treatment
|
Quenched&Tempered Steel Plate
|
Thickness
|
Common 2~100 mm (1~300 mm)
|
Width
|
Common 10~2500 mm (600~2500 mm)
|
Length
|
100~12000 mm, customized
|
surface
|
Clean, finishing,blasting and painting according to customer requirement
|
Certificate
|
MTC will be provided with goods, third part inspection is acceptable, for example BV,SGS.
|
Trading term
|
EXW, FOB, CFR, CIF
|
Application
|
Widely used in a variety of architectural and engineering structures,such as
1.) metal constructions such as buildings,bridges,ships; 2.) transmission tower, reaction tower; 3.) lifting transportation machinery; 4.) industrial furnace;boilers 5.) container frame, warehouse goods shelves, etc |
GB/T 24186 NM Wear Resistant Steel Plates Chemical Composition(%) max.
|
|||||||||
Grade
|
C
|
Si
|
Mn
|
P
|
S
|
Cr
|
Ni
|
Mo
|
Ti
|
NM300
|
0.23
|
0.70
|
1.60
|
0.025
|
0.015
|
0.70
|
0.50
|
0.40
|
0.050
|
NM360
|
0.25
|
0.70
|
1.60
|
0.025
|
0.015
|
0.80
|
0.50
|
0.50
|
0.050
|
NM400
|
0.30
|
0.70
|
1.60
|
0.025
|
0.010
|
1.00
|
0.70
|
0.50
|
0.050
|
NM450
|
0.35
|
0.70
|
1.70
|
0.025
|
0.010
|
1.10
|
0.80
|
0.55
|
0.050
|
NM500
|
0.38
|
0.70
|
1.70
|
0.020
|
0.010
|
1.20
|
1.00
|
0.65
|
0.050
|
NM550
|
0.38
|
0.70
|
1.70
|
0.020
|
0.010
|
1.20
|
1.00
|
0.70
|
0.050
|
NM600
|
0.45
|
0.70
|
1.90
|
0.020
|
0.010
|
1.20
|
1.00
|
0.80
|
0.050
|
B: 0.0005-0.006, Als min. 0.010
|
GB/T 24186 NM Wear Resistant Steel Plates Mechanical Properties
|
||||
Steel Grade
|
Thickness
|
Hardness (HBW)
|
Elongation
|
Tensile Strength
|
NM300
|
≤80
|
270-330
|
≥14%
|
≥1000 Mpa
|
NM360
|
≤80
|
330-390
|
≥12%
|
≥1100 Mpa
|
NM400
|
≤80
|
370-430
|
≥10%
|
≥1200 Mpa
|
NM450
|
≤80
|
420 - 480
|
≥7%
|
≥1250 Mpa
|
NM500
|
≤70
|
≥470
|
-
|
-
|
NM550
|
≤70
|
≥530
|
-
|
-
|
NM600
|
≤60
|
≥570
|
-
|
-
|
Grade Comparison
|
|
GB
|
NM300,NM360,NM400,NM450,NM500
|
SS
|
HARD400, HARD450, HARD500, HARD600
|
DIN
|
XAR400, XAR450, XAR500, XAR600, Dillidur400, Dillidur500
|
NBN
|
QUARD400, QUARD450, QUARD500
|
NF
|
FORA400, FORA500, Creusabro4800, Creusabro8000
|
JIS
|
JFE-EH360, JFE - EH400, JFE - EH500, WEL-HARD400, WEL-HARD500
|
SFS
|
RAEX400, RAEX450, RAEX500
|